PA66 black virgin, PA66, Nylon 66, Polyamide 66, Engineering Polymers

PA66 black virgin , PA66, Nylon 66, Polyamide 66, Engineering Polymers PA66 glass fiber reinforced nylon is made of PA66 resin and filled with 10-40% glass fiber. It is of high strength, durability, wear resistance and corrosion resistance. In addition, the material is dimensionally stable with high temperature thermal deflection, good

PA66 black virgin, PA66, Nylon 66, Polyamide 66, Engineering Polymers

PA66 black virgin glass fiber reinforced nylon is made of PA66 resin and filled with 10-40% glass fiber. It is of high strength, durability, wear resistance and corrosion resistance. In addition, the material is dimensionally stable with high temperature thermal deflection, good electrical insulation, good smooth surface, easy molding and other advantages. RoHS approved material is compliant and can be widely used in auto parts, electrical equipment, power tools, gears, mechanical parts and other fields.

Specification:

Item Typical Characteristic Testing   Standard
Density 1.18g/cm3 ASTM D-792
 Molding Shrinkage 1.0-1.5%
at 23℃
ASTM D-955
Water Absorption 8.50% ASTM D-570
Moisture absorption 2.30% ASTM D-570
Tensile Strength 86MPa ASTM D-638
Elongation at break 2.0-5.0%
at 10mm/min
ASTM D-638
Flexural Strength           105MPa ASTM D-790
Flexural Modulus 2970MPa ASTM D-790
Izod Notched Impact Strength 36J/m ASTM D-256
Friction Coefficient 0.2
+73□H(+23℃) Static
Thrust Washer Test3
Friction Coefficient 0.35
+73□H(+23℃) Dynamic
Thrust Washer Test3
Melting Point 260℃ ASTM D-3418
Heat Deflection Temp 230℃ ASTM D-648

Processing:

Molding Injection

 

Item DIN Method Units Valus
Density D 53479 g/cm3  1.13
Mold Shrinkage D 53464 Mm/mm  0.013
Tensile Strength D 53455 Mpa  80
Strain at break D 53455 %  25
Flexural Strength D 53452 Mpa 100
Flexural Modulus D 53457 Mpa  2700
Izod impact Strength D 53453 KJ/m2  4.4
Dielectric Strength D 53481 kv/mm  20
Melting Point  — °C  260
Fire Resistance UL 94   HB  —
Filler Method for
ignition
  %  30

 

Packing: 30Kg/1000 kg net bags as customer request

Product usage:
It serves as an ideal raw material for automobile parts, ribbon sports goods,
plug connector, Instrument equipment

 

With ISO9001:2015, OHSAS18000, ISO14001, TS16949 Quality Management system certification of partial products, all materials applied have been certified by such authoritative organizations as SGS and have passed ROHS and REACH to ensure that clients acquire high-quality material.

Reviews

There are no reviews yet.

Be the first to review “PA66 black virgin, PA66, Nylon 66, Polyamide 66, Engineering Polymers”

Your email address will not be published.